UV Adhesive Loxeal 3023, 100ml
Article: M-03.01.004
Рейтинг: 5
Price: 1 700.00 grn
Very low viscosity, fast curing, high strength Ultra Violet curing adhesive. Specially designed for bonding float glass to glass and glass to metal in glass and crystal furniture manufacturing.
Physical properties
Composition: methacrylate ester
Colour : clear/colourless
Viscosity (+25°C-mPas) : 50-100
Specific weight (g/ml): 1,02
Curing timeUV (365 nm) : 8-15seconds
Gap to fill: 0,03 mm /1,5 mm
Flash point: >+100°C
Shelf life : 1 year at +25°C in original unopened packaging
Curing properties
To obtain the best features, clean and dryparts to bond. The polymerisation UV is belonging to the intensity of the UV lamp, to the distance from the UV light source, to the bondline gap and to the ligth transmittance of the substrate the light shall pass through. We recommend high inensity UV light sources with minimum radiation between 365 nm and 420 nm at 100mW/cm2. Curing time may vary according to adhesive gap.
Properties of cured adhesive
Tensile strength (ASTM D-2095-69): 10-14 N/mm²
Elongation at break (DIN 53504) : 60100%
Hardness (Shore D) : 65-75
Temperature range: -55°C/+120°C
Light transmittance: > 98%
Coefficient of thermal expansion: 85 x 10-6mm/mm/°C
Dieletric constant (+25°C 1000 Hz): 4
Dieletric strength: 10-12 kV/mm
Features
Тип химического соединения |
уретаново-метакрилатный эфир |
Цвет | бесцветный, прозрачный |
Вязкость при 25ºС | 80-150 сПз |
Удельный вес (при при 25ºС) | 1,1 г/см3 |
Время схватывания (начальная прочность) | 45 сек. |
Время набора полной прочности | через 12 ч. |
Величина монтажного зазора | 1,5мм |
Прочность при разрезании (DIN53283) | 10-14 H/мм2 |
Коэфициент преломления | 1.49-1.51 |
Диапазон рабочих температур | от -55ºС до +120ºС |
Производство | Италия |
//